One of the most studied atomic ordering is CuPt type ordering in III-V semiconductor alloy in chemistry and physics. It occurs in III-V alloy when the cation planes take an alternate sequence of A-rich and B-rich plane following AxB1−xC. The resulting structure is usually called as superlattice-like structure along [1-11] or [-111] – called (111) B plane, or along [-1-1-1] or [11-1] – called (111) A plane. The two ordering direction is thus called CuPt type A and B ordering.
Attributes | Values |
---|
rdfs:label
| - Cu-Pt type ordering in III-V semiconductor (en)
|
rdfs:comment
| - One of the most studied atomic ordering is CuPt type ordering in III-V semiconductor alloy in chemistry and physics. It occurs in III-V alloy when the cation planes take an alternate sequence of A-rich and B-rich plane following AxB1−xC. The resulting structure is usually called as superlattice-like structure along [1-11] or [-111] – called (111) B plane, or along [-1-1-1] or [11-1] – called (111) A plane. The two ordering direction is thus called CuPt type A and B ordering. (en)
|
foaf:depiction
| |
dcterms:subject
| |
Wikipage page ID
| |
Wikipage revision ID
| |
Link from a Wikipage to another Wikipage
| |
sameAs
| |
dbp:wikiPageUsesTemplate
| |
thumbnail
| |
has abstract
| - One of the most studied atomic ordering is CuPt type ordering in III-V semiconductor alloy in chemistry and physics. It occurs in III-V alloy when the cation planes take an alternate sequence of A-rich and B-rich plane following AxB1−xC. The resulting structure is usually called as superlattice-like structure along [1-11] or [-111] – called (111) B plane, or along [-1-1-1] or [11-1] – called (111) A plane. The two ordering direction is thus called CuPt type A and B ordering. The same type ordering is also observed in II-VI alloy such as CdZnTe alloy. The ordering sequence viewed on atomic planes along [-111] and [1-11] reveals Cd and Zn alternating planes. This ordering reduces the lattice symmetry ordering to L11 and leads to change of its optical and electrical properties. The apparent effects are: band gap reduction, valence band splitting, and optical anisotropy. For instance, in CuPt type B ordering, the L point of the Brillouin zone fold back to the Γ-point, and the folded band “repels” the original conduction band minimum and bring down the bottom of conduction band. AlInP epilayers grown by metal-organic vapour-phase epitaxy on GaAs substrates exhibit CuPt-B-type spontaneous atomic ordering. Additionally, CuPt-type structures were observed in CdZnTe during metal-organic vapor phase epitaxy. (en)
|
gold:hypernym
| |
prov:wasDerivedFrom
| |
page length (characters) of wiki page
| |
foaf:isPrimaryTopicOf
| |
is Link from a Wikipage to another Wikipage
of | |
is Wikipage redirect
of | |
is foaf:primaryTopic
of | |